First,the characteristics of the product
SiliconQK-3013is transparenttwo-component,high strength,high transparency,hightearresistance,soft hand feeling,strong adhesion,small shrinkage rate,operationaltime up to 20 hours ofnewsilicone
labelrubber;new materialused in Japanadvanced technology(is currently widely used in thethree-dimensionaltrademark printing,clothing.Printerribbon,silk screenprinting,qualityproducts).Forvery
complex shapeandhigh precisionmodel.
Two,property
★ hightransparent;
★small shrinkage;
★two method:
(1),the standard type(2),the
machinemixing
★ifmaking speedto control orslow downtothe
deployment ofcuring agentamount;
★ifmaking speedto control orslow downtothe
deployment ofcuring agentamount;
Three,application
★suitable forcloth standard,anti-counterfeit trademarksandsilk
screenprintingsilica gel;
★suitable for
environmental protectionbrand
trademark,stereoscopic trademark;
Control
device,moresuitable for automobile industryheatingdevice,decorative lights,etc..
Four,technical indicators
|
Solids content |
% |
100 |
|||
|
Mixed viscosity |
|||||
|
mPa.s |
35,000 |
||||
|
As molded |
|||||
|
D7921 |
|||||
|
Specific gravity |
1.09 |
||||
|
D2241 |
|||||
|
Hardness |
Shore A |
33 |
|||
|
D4112 DIE C |
|||||
|
Tensile strength |
MPa (psi) |
4.5 (725) |
|||
|
D4112 DIE C |
|||||
|
Elongation at break |
% |
400 |
|||
|
D6214 DIE B |
|||||
|
Tear strength
Volume
resistivity |
kN/m (Ppi)
Ohm.cm
|
5(40)
4.5xl0l5
|
|||
TheA,Bagent10:1 by weightare mixed uniformly,andvacuum
exhaustbubble.
Thecuring time and temperature:205 ° C/15-40seconds(for reference only,please considerthe actual operation.).
●operatingtime is 20 hours.
Six,packaging
Theproduct packaging for 20kg/.
Direction
for use :
Use ratio of A and B = now, before the use should be A, B
component in proportion to fully mix evenly, quiet place TuoPao or vacuum
TuoPao.
Don't touch the containing N, P, S plasma compounds and contain
alkynyl and vinyl compounds, lest make, platinum catalyst poisoning and cannot
cure, especially PVC contains Pb (lead), can make the catalyst poisoning some
organic pigments can also lead to curing slowed or not curing.